PRODUCT TYPE

HODT MULTI FILM is a diluted hybrid system, which contains as well a physically drying dispersion as a water-soluble, oxidative hardening binder system.

COLOR

Clear, Black

HANDLING

With brush, roller or airless spraying a dry thickness of at least 100 μm should be reached. HODT MULTI FILM can be diluted with water if necessary. After dilution however you should apply several coats in order to get the required thickness. After 1-2 hours it is touch-dry and after 24 hours it can be recoated depending on temperature and humidity.

CHARACTERISTICS

• Single component product with excellent adhesion and elasticity
• Primer (recoatable) and topcoat
• Without solvents
• Oxidative hardening
• Economical and uncomplicated in application. In one orperation a thickness of 30 until 50 μm can be applied. (by spray or immersion processes)
• Can be diluted with water in any ratio in order to achieve a thin layer thickness (e.g. on threads)
• High elasticity of the coating ensure that no cracks or chipping during the expansion and contraction of the material appear
• Meets the highest requirements for chemical and mechanical resistance. The coating provides a hard, abrasion-resistant, elastic varnishing with excellent resistance against corrosion, solvents, diluted acids and alkaline solutions etc.. It adheres to nature and synthetic rubber, polyethylene, pvc

SURFACE PREPARATION

Apply only on degreased, cleaned surface. Applicable also on seized rust. For information about the precise procedure please take a look at our technical data sheet.

FIELDS OF APPLICATION

• Protection of metal surfaces as primer and topcoat
• Additional protection of coated surfaces against environmental influences and mechanical damage
• Transparent corrosion protection for the maintenance of original Patina

STORAGE

To be stored frost-free. At temperatures up to 25° the original packed goods are at least storable for 1 year.

PRODUCT TYPE

• Corrosion preventative with lubricant- and rust moving properties
• Based on lanolin
• Physiologically non-hazardous

COLOR

clear, shiny

HANDLING

Spraycan with small spray applicator and 60 cm cavity probe

CHARACTERISTICS

• Penetrates rapidly, nevertheless adheres well.
• Does not evaporate nor resinify as it is usual by most of penetrating oils
• Temperature-stable
• Requires a minimum surface preparation and forms a protection film
• Penetrates rust, displaces water and forms a resistant corrosion protection
• Good adhesion on wet and dry surfaces protection film does not dry out
• Excellent resistance against rain and salt water, but can be easily removed if required
• Quick operational readiness after application
• In case of damnifi cation of the coating FLUID FILM AS-R has limited self healing effects FLUID FILM AS-R spraycan (400 ml) meets the regulations MIL-C-23050, paragraph 3.6.

FIELDS OF APPLICATION

Indispensable for plants, work shops, garages and do-it-yourselfers:

• On the automotive it protects hinges, batteries, door-edges, cavities, engine compartments as well as all other parts exposed to corrosion
• Particularly recommended for winterizing, already a light coat protects chains from wear and corrosion
• Inhibits corrosion on all metal surfaces as for example: on tools and machines.
• Provides optimal corrosion protection on boat-engines and other boat-parts exposed to corrosion.
• As lubricant and preservative it is especially suitable for all moving parts such as guide rollers, chain conductions from rudders, hinges and so on.
• For maintenance of guns and for sport-, recreationand home equipment
• As corrosion protection of steel and metal parts during transport, storage and processing in production plants
• As pretreatment for underbody protection Plastifies and activates already existing bitumen protective layer on the underbody of vehicles

PRODUCT TYPE

• Solvent free, thixotropic corrosion preventative
• Based on lanolin
• Physiologically non-hazardous

COLOR

Clear, shiny

HANDLING

Spraycan with small spray applicator and 60 cm cavity probe

CHARACTERISTICS

• Suitable for lubricant and penetrating oil
• Requires less surface preparation and forms a protection film
• Can be applied as rust remover as well as rust protection
• Penetrates rust, displaces water and forms an extremely resistant protection against corrosion caused by salt
• Good adhesion on wet or dry surfaces
• No evaporation, resinifying or drying of the protection coat
• Excellent resistance against rain and salt water, but can be easily removed if required
• Can get into contact with water immediately after application
• In case of damnification of the coating FLUID FILM has limited self healing effects
• FLUID FILM NAS meets the regulations of the United States Militay Specification- MIL-C-16173

FIELDS OF APPLICATION
Single layer anticorrosive coating. Mainly destined for protection of cavities, metal surfaces for in-plant temporary storage and for preservation during sea and road transport, winter service and pretreatment for underbody protection. Also applicable as lubricant and penetrant. Conventional treatment by spraying, brush or roller for corrosion preventative measures on dry or wet, bare or rusty surfaces to be protected against salt water and climatic influences.

PRODUCT TYPE

Calcium sulfonate complex

COLOR

Aluminium, black, buff and transparent

APPLICATION

Spray gun or brush / roller and by airless spraying

CHARACTERISTICS

• Corrosion preventive and topcoat in one
• Can be applied directly in system with FLUID FILM Liquid A / NAS or AS-R (Spray) on existing deep-seated rust. The excellent penetration properties of the system warrant a thoroughly wetting and encapsulation of rust and/or already existing coatings
• Long-term corrosion protection
• Good wettability on deep porous surfaces as well as on joints and folds (seam sealing) in system with pre-primer FLUID FILM as thinner
• High thickness layers can be easily reached in one coat when applied by airless spraying
• High tolerance against relative humidity during application (possible near the dew point), and salt water resistance
• High solids content and mild solvent in the formulation Low material loss
• Due to the compatibility with deep penetrating FLUID FILM, PERMA FILM system can be applied with a considerably lower standard of surface preparation as required by usual colour coatings
• Application possible at low temperatures (O°C)

FIELDS OF APPLICATION

• Ballast water tanks
• Industrial facilities
• Wheel house
• Winter road service & equipment
• Underbodies

PRODUCT TYPE

• solvent free coating
• on lanolin basis
• physiologically non hazardous

COLOR

Transparent

HANDLING

With standard compressed air systems without heating the material, with brush/roller or by floatation

CHARACTERISTICS

• Can be applied by floatation or any other conventional
• handling method
• Forms with water or air humidity a gel
• Requires minimum surface preparation and forms a protective film
• Penetrates rust, displaces water and forms a resistant corrosion protection
• Good adhesion on wet or dry surfaces
• No evaporation, resinifying or drying out of the protective film
• Is not washed off by rain or seawater, but can easily be removed, when required
• Quick operational readiness after application
• As a primer in system with PERMA FILM
• As a base coat for heavily rusted wire ropes and cables
• In case of injuries of the coating, FLUID FILM Liquid A shows a limited self-healing effect.
• FLUID FILM Liquid A corresponds to the United States Military Specification – MIL-C-16173

FIELDS OF APPLICATION

Single layer anticorrosive coating – mainly for floating of ballast water tanks in need of repair on ships, floating docks, offshore units, body inside protection of cars etc., where a compromise between effort and protective effect has to be made. Furthermore suitable for screw connections, seams, overlapping areas, stockage in winter, winter service, cavity sealing, storage and transport of metal parts. In case of conventional handling by means of spraying devices, brushes or rolls for anticorrosive measures on dry or humid, blank or rusty surfaces, which have to be protected against saltwater and against any atmospheric conditions.